Fortunately, there are several parts of design such as hinges, fiber optic connector bases, and new style connectors are closely dependent on MIM technology. These products are being produced in a large number and MIM technology is being adopted by more and more.
MIM and CIM--Drome can provide one-stop service solution.
The basic attributes include:
1.Economical production of complex parts with weight from 0.03 to 200g from high-performance engineering materials.
2.Parts with high dimensional precision (±0.1%~±0.5%) and good surface quality (surface roughness 1~2μm).
3.Parts with high relative density (96%~100%), homogeneous microstructure and superior performance.
4.Adaptable to powders of various materials and wide application of the parts.
5.Material saving through the recycle of wastes, production process with high level of automation and suitable for mass production
Flow chart of metal injection molding
Application of MIM
Products Range:
Â
| Material | Â | Typical Values | Â | Â | ||||
| Designation Code | Density g/cm3 | Tensile Properties | Young's modulus, Gpa | Un-notched Charpy Impact Energy,J | Hardness,Rockwell | |||
| Â | Â | UTS. Mpa | Y.S. (0.2%), Mpa | Elongation (in 25.4mm) % | Â | Â | Macro (apparent) | Â Micro (converted) |
| MIM-Fe2Ni | 7.8 | 280 | 115 | 25 | Â | Â | 55 HRB | 50HRCÂ Â Â Â |
| MIM-Fe8Ni | 7.8 | 450 | Â | 12 | Â | Â | 84HRB | 50HRCÂ Â Â Â |
| MIM-2200 (as sintered) | 7.8 | 290 | 125 | 40.0 | 190 | 135 | 45 HRB | Â |
| MIM-2700 (as sintered) | 7.8 | 415 | 255 | 26.0 | 190 | 175 | 69 HRB | Â |
| MIM-4605 (as sintered) | 7.8 | 440 | 205 | 15.0 | 200 | 70 | 62 HRB | Â |
| MIM-4605 (Q&T) | 7.8 | 1655 | 1480 | 2.0 | 205 | 55 | 48 HRC | 55 HRC |
| MIM-304L | 7.8 | 500 | Â | 70 | Â | Â | 60 HRB | Â |
| MIM-316L (as sintered) | 7.85 | 520 | 175 | 50.0 | 190 | 190 | 67 HRB | Â |
| MIM-410 | 7.7 | 900 | Â | 7 | Â | Â | Â | 40 HRC |
| MIM-420 (heat treated) | 7.7 | 1380 | 1200 | 12 | 190 | 40 | Â | 45-60HRC |
| MIM-430L (as sintered) | 7.8 | 410 | 240 | 25.0 | 210 | 150 | 65 HRB | Â |
| MIM-440C | 7.8 | 700 | 590 | 15 | Â | Â | Â | 45-60HRC |
| MIM-17-4PH (as sintered) | 7.8 | 900 | 730 | 6.0 | 190 | 140 | 27 HRC | Â |
| MIM-17-4PH (heat treated) | 7.8 | 1190 | 1090 | 6.0 | 190 | 140 |
This series of equipment is oriented to the gold-loaded carbon in the gold cyanide carbon slurry process for gold desorption and electrolysis, and the gold adsorbed on the gold-loaded carbon is produced in the form of high-grade gold mud. This series of equipment has 3 patented technologies and 5 proprietary technologies. Sodium cyanide is not used in the desorption liquid, which reduces the lean carbon grade below 100g/t. The key technology of this equipment is to ensure the balance of metal content, avoid the phenomenon of equipment "accumulation" and "floating gold", and ensure the stable and stable technical indicators of the equipment. The cost is low, and the content of technological advancement has been broadcast on the Spark Science and Technology column of CCTV in 2000. The technology passed the technical appraisal in 2003 and won the second prize of Science and Technology of the China Gold Association. The overall technical level is domestically leading. In 2006, it was designated as an energy-saving technology for gold production by the National Development and Reform Commission. In 2007, it was designated as an industry standard equipment by the National Development and Reform Commission. The equipment has obtained 3 Chinese patents, the patent numbers are: 01241537.5 01241538.5 200620029209.1